THE INFLUENCE OF THE DEPTH OF SUBSTRATE DENTIN SURFACE AND THICKNESS OF THE CURRENT RESTORA TIVE SAMPLES ON BOND STRENGTH
THE INFLUENCE OF THE DEPTH OF SUBSTRATE DENTIN SURFACE AND THICKNESS OF THE CURRENT RESTORA TIVE SAMPLES ON BOND STRENGTH
 
لغة الوثيقة : الانجليزية 
المستخلص : The effect of sample thickness and dentin depth on bond strength of composite, compomer and resin modified glass ionomer have been investigated. The occlusal surfaces of 84 non carious human third molars were used for bonding. 4 subgroups were tested, superficial dentin with sample thickness 1 and 2 mm and deep dentin with sample thickness 1 and 2 mm respectively SBMP + /z100 composite showed 26 + 3.2,22.3 + 4.5, 17 + 3.2 and 21.8 + 4.2 MPa shear bond strength to S.dentin 1 mm, Deep dentin 1 and 2 mm and S. dentin 2 mm respectively . Compoglass reported 10.4 + 1.57, 9.1 + 2.3, 5.0 + 0.6 and 9.24 + 3.1 MPa while, vitremer achieved 4.7 + 0.49, 3.2 + 0.39. 3.0 + 0.53 MPa. It is concluded that the highest bond strength can be achieved to superficial dentin in thickness or increments not more than 1 mm. and that both dentin depth and sample thickness might influence the quality of the bond to dentin with an effect that varies from one material to aanother depending upon the mechanism of bond of each material and it's chemical composition. 
ردمد : 0 
اسم الدورية : Egyptian Dental Journal 
المجلد : 41 
العدد : 4 
سنة النشر : 1995 هـ
1995 م
 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Wednesday, June 18, 2008 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
هاني شمسShams, Hani باحثدكتوراهhsalamah@kau.edu.sa

الملفات

اسم الملفالنوعالوصف
 THE INFLUENCE OF THE DEPTH OF SUBSTRATE.pdf pdf 

تحميل الصفحة

الرجوع إلى صفحة الأبحاث